- concrete restoration in accordance to DIN EN 1504-3
- ready-to-use restoration mortar
- reduces the penetration of CO2
- Construction material class A1 (non flammable) in accordance to DIN 4102-1 and EN 13501
- RM02: corrosion protection and bonding bridge
SM20 sprayable mortar (SPCC)
SPCC concrete substitution system in accordance to ZTV-ING part 3, section 4, DAfStb directive SIB M2 as well as directive IH and EN 1504-3 for structurally non-relevant purposes
- granularity: 0-2 mm
- layer thickness: 10-50 mm
- consumption: 1,85 kg/(m²⋅mm)
- processing time at 20°C (68 °F): about 45 min
- compressive strength after 28 d: ≥ 50 N/mm²
properties
- ready-to-use repairing mortar, needs only to be mixed with water
- reduces the penetration of CO2 and humidity (anti-carbonation), to great extent impermeable to oil and water, at the same time provided with large reserves of alkali, active protecting the reinforcement against corrosion, and resistant to saponification
- soft plastic consistence while processing with dense-flow wet-spraying method and very good firmness in vertical and overhead surfaces
- supplied as system comprising the following components:
- RM02 CORROSION PROTECTION AND BONDING BRIDGE
- SM20 SPRAYED MORTAR (SPCC) (0-2,0 mm)
- MS05 PCC FILLER / PUTTY (0-0,5 mm)
fields of application
- concrete repair, reinforced concrete and pre-stressed concrete in the MAWO-PAGEL DENSE-FLOW WET-SPRAYING PROCESS in bridges and civil-engineering structures
- repair pillars damaged by chloride in parking houses and underground garages in the MAWO-PAGEL DENSE-FLOW WET-SPRAYING PROCESS
- increasing of the coating of the reinforcement of concrete, for improving the fire resistance (material class A1, non-flammable)