- hardens quickly, can bear loads very early
- impermeable to water and to great extent mineral oil and fuel resistant
- RM02: corrosion protection
- IH10: bonding bridge for industrial floors
- residual moisture after 24 hours ≤ 4,0 % (calcium carbide method)
IB20 industrial floor
ready-to-use, low-shrinkage, abrasion-resistant industrial floor in accordance with DIN EN 13813 for stress groups II and III
- granularity: 0-2 mm
- layer thickness: 10-100 mm
- consumption: 2,00 kg/(m²⋅mm)
- processing time at 20°C (68 °F): about 30 min
- compressive strength after 28 d: ≥ 60 N/mm²
- abrasion: 7 cm³/50 cm²
properties
- ready-to-use mortar for industrial floors, just mix with water
- easy to apply
- quick hardening, rapidly capable of bearing weight
- low shrinkage
- abrasion resistant
- impermeable to water and to great extent mineral oil and fuel resistant
- stress group II and III (DIN 18560-7)
- residual moisture after 24 hours < 4 % (calcium carbide method)
- satisfies the requirements of the type A1 construction materials (non-flammable) according to the ruling 2000/605/EG of the European Commission, September 26th 2000 (published in official journal, L258)
fields of application
- industrial floor subject to high loads
- hangars
- parking buildings
- repairshops and garages
- exhibition halls
- market halls